|Product:||17-7PH 631 Cold Rolled Stainless Steel Sheet And Coil||Size Range:||0.1~3.0X5~420mm|
|Delivery Condition:||A, C||Specification:||ASTM A693, AMS 5528, 5529|
630 stainless steel,
17 7 ph stainless steel
17-7PH UNS S17700 Cold Rolled Stainless Steel Sheet SUS631 Strip Condition C
Precipitation hardening steel W.-nr. 1.4568 DIN X7CrNiAl17-7, AISI 631, UNS S17700, 17-7PH
is a corrosion resistant steel with good formability in soft condition.
The work hardening is greater than other austenitic stainless steels, similar to 1.4310.
The use of stainless 1.4568 is indicated, if stress applied parts were exposed to higher temperatures
or if spring parts have to be formed in soft condition with additional hardening.
Please contact our technicians for details.
For machining high quality tooling is required, like for all stainless steels. Polishing is possible.
1.4568 stainless supplied in annealed condition shows low magnetism witch increases with cold forming.
In hard condition: Highly stressed spring parts. Spring parts exposed to higher temperature.
In soft condition: Spring parts which have to be formed in soft condition (spring back effect).
Standard and specifications
|AISI, UNS||EN, DIN||JIS||Chemical composition %wt typical|
|17-7PH, S17700||1.4568, X7CrNiAl17-7||SUS631||C 0.07, Si 0.6, Mn 0.8, Cr 17.0, Ni 7.0, Al 1.0|
DIN EN 10 088-2 Stainless steels - part 2 technical delivery conditions for sheet/plate and strip of corrosion resisting
steels for general purposes
DIN EN 10151 Stainless steel strip for springs
ISO 6931 - 2: Stainless steels for springs — Part 2: Narrow strip
JIS G4313: Cold rolled stainless steel strip for springs
Typical mechanical values at room temperature, solution annealed:
Tensile strength Rm: 700 – 850 MPa
0,2 % Yield point Rp0,2: 270 – 350 MPa
Elongation A80: >35 %
For Details, please Contact
WUXI GUANGLU Special Steel Co., Ltd.
Stainless martensitic • precipitation hardening steel • stainless ferritic — Our answer to your needs
Tel: +86 510 81812873
Contact Person: Paul Lu