JIS SUS405 ( EN 1.4002 ) Hot Rolled Stainless Steel Sheets / Plates Cut Lengths
JIS SUS405, EN 1.4002, AISI 405, UNS S40500 is a 13% chromium steel, designed to be used in the
as welded condition. Unlike other grades in the 13% chromium category, stainless 405 is not susceptible to
extensive hardening through air cooling from high temperature.
Commonly used for annealing boxes, steam nozzles, quenching racks, partitions and other fabrications that
cannot be annealed after welded.
Soft and ductile, 405 stainless alloy can be easily machined using most standard practices.
Experienced machinists comment that 405 stainless machines similarly to 4130 alloy steel.
405 can be easily spun, drawn and formed using common forming procedures.
405 ( 1.4002 ) can be welded using shielded fusion and resistance techniques.
Oxyacetylene welding is not recommended.
Use 405 Cb electrodes that contain columbium rather than aluminum to control hardening.
Post weld annealing will maximize ductility.
Soak at 1500-1600 F(817-871 C) and then quickly increase to 1900-2050 F(1038-1121 C).
Do not remain at this temperature as the result will be excessive grain growth. Do not work below 1500 F(816C).
After forging, air cool and anneal.
AISI Type 405 1.4002 has marginal stainless steel corrosion resistance. It is used primarily as a structural material.
It is serviceable in continuous service up to 1300 F and in intermittent exposures up to 1500 F.
It does not harden appreciably when air cooled from high temperature where some austenite may exist.
stainless 405 is a 13% chromium steel designed to be used in the as-welded condition.
Unlike other 13% chromium stainless steels, it is not subject to a great deal of hardening through air cooling form high temperatures.
| Grade | C | Cr | Al |
| SUS405 | 0.08 | 11.50~14.50 | 0.10~0.30 |
Forms
JIS SUS405 stainless steel sheet/plate/strip/coil
ASTM A268 TP405 seamless stainless steel tube
For Details, please Contact
WUXI GUANGLU Special Steel Co., Ltd. ( Stainless martensitic • precipitation hardening steel • stainless ferritic — Our answer to your needs )
Tel: +86 510 81812873
Email: export@guanglusteel.com
Contact Person: Mr. Paul
Tel: 86-510-81812873
Fax: 86-510-81812872