FV520B 1.4594 S45000 S143/4/5 Hot Forged And Rolled Stainless Steel Round Bar
FV520B is a martensitic precipitation hardening stainless steel. It is similar to the more common
PH stainless grade 17-4PH.
FV520B has useful corrosion resistance in modest corrosion environments having similar characteristics
to that of austenitic stainless steel grades. It has useful resistance to some acid conditions and
has low rusting rate in marine and industrial atmospheres.
FV520B has good weldability characteristics when using standard techniques.
Oxy-acetylene welding is not recommended due to the possible pick up of carbon.
We recommend you contact your welding consumables supplier who should provide you full assistance
and information on welding FV520B stainless steel.
Typical applications include pump shafts, impellers, fasteners, fans, valves, hydraulic equipment
used in oil and gas industries, petrochemical, marine and nuclear engineering, and aircraft
components such as steam turbine blades.
Chemical composition ( weight % )
Grade | C | Si | Mn | P | S | Cr | Ni | Mo | Cu | Nb |
FV520B | 0.07 max | 0.70 max | 1.00 max | 0.035 max | 0.025 max | 13.20~14.70 | 5.00~6.00 | 1.20~2.00 | 1.20~2.00 | 0.20~0.70 |
Typical Automated Properties
Condition | 0.2% Proof Stress N/mm² | Tensile Strength N/mm² | Elongation % min | Hardness Brinell HB | Izod Joules min |
Primary Hardened 1050º C +2 hours 750-850ºC | - | - | - | 293-341 | - |
Double Overaged 1050º C +2 hours 750-850ºC +2 hours 550ºC | 800 | 925-1090 | 15 | 277-341 | 54 |
Heat treatment
Heat assay temperatures, including amount of heating, cooling and assimilation times will alter due to factors
such as the appearance and admeasurement of anniversary steel component.
Added considerations during the calefaction assay action cover the blazon of furnace, abatement boilerplate
and plan breadth alteration facilities. Amuse argue your calefaction assay provider for abounding advice on
calefaction assay of FV520B stainless steel.
Form of supply
stainless steel bar FV520B
For Details, please Contact
WUXI GUANGLU Special Steel Co., Ltd.
Stainless martensitic • precipitation hardening steel • stainless ferritic — Our answer to your needs
Tel: +86 510 81812873
Email: export@guanglusteel.com
Contact Person: Mr. Paul
Tel: 86-510-81812873
Fax: 86-510-81812872