EN 1.4568 DIN X7CrNiAl17-7 SUS631 Cold Rolled Stainless Steel Strip In Coil

Guanglu is really a professional supplier, they always give us technical advice and provide good quality products with very competitive price!

—— Thomas Hoover

We received your goods last thursday and we are very pleased with the quality of your products.

—— Lionel Lobo

I'm Online Chat Now

EN 1.4568 DIN X7CrNiAl17-7 SUS631 Cold Rolled Stainless Steel Strip In Coil

EN 1.4568 DIN X7CrNiAl17-7 SUS631 Cold Rolled Stainless Steel Strip In Coil
EN 1.4568 DIN X7CrNiAl17-7 SUS631 Cold Rolled Stainless Steel Strip In Coil EN 1.4568 DIN X7CrNiAl17-7 SUS631 Cold Rolled Stainless Steel Strip In Coil

Large Image :  EN 1.4568 DIN X7CrNiAl17-7 SUS631 Cold Rolled Stainless Steel Strip In Coil

Product Details:
Place of Origin: China
Brand Name: Daway
Certification: SGS
Model Number: EN 1.4568 DIN X7CrNiAl17-7 SUS631
Payment & Shipping Terms:
Minimum Order Quantity: 500 kgs
Price: negotiable
Packaging Details: seaworthy
Delivery Time: 15 days after receipt 30% of value
Payment Terms: T/T
Supply Ability: 200 tons per month
Detailed Product Description
Material: EN 1.4568 DIN X7CrNiAl17-7 SUS631 Cold Rolled Stainless Steel Strip In Coil Dimension: 0.1~3.0mmx5~420mm
Delivery State: ANN, Condition C ( 1/2H, 3/4H H ) Surface: Bright
High Light:

630 stainless steel

,

17 7 ph stainless steel

EN 1.4568 DIN X7CrNiAl17-7 SUS631 Cold Rolled Stainless Steel Strip In Coil

DIN 1.4568 is a corrosion resistant stainless steel with good formability in soft condition.
The work hardening is greater than other austenitic stainless steels, similar to 1.4310.
The use of 1.4568 stainless is indicated, if stress applied parts were exposed to higher temperatures

or if spring parts have to be formed in soft condition with additional hardening. 
DIN 1.4568 stainless strip in annealed condition shows low magnetism witch increases with cold forming.
 
Typical applications
In hard condition: Highly stressed spring parts. Spring parts exposed to higher temperature.
In soft condition: Spring parts which have to be formed in soft condition (spring back effect).

 

Precipitation hardening steel, Stainless Chromium – Nickel - Steel
DIN EN 10 088-2: Technical delivery conditions for sheet/plate and strip of corrosion resisting steels for general purposes
DIN EN 10151: Stainless steel strip for springs
ISO 6931 - 2: ISO 6931-2 : Stainless steels for springs, cold-rolled narrow strip of thicknesses up to and including 3 mm, in rolled widths less than 600 mm, made from stainless steel.
EN 1.4568, DIN X7CrNiAl17-7
ASTM 631, AISI S17700 (UNS) (USA)
JIS G4313: Cold rolled stainless steel strip for springs
SUS 631-CSP (Japan)

 
Chemical composition ( typical weight % )

Grade C Si Mn Cr Ni Al
1.4568 0.07 0.60 0.80 17.0 7.0 1.0

 
Product forms
1.4568 stainless is produced as narrow strip ( precision strip ) in the thickness range from 0.1 mm to 3.0 mm.
The possible width is in between 5 mm to 420 mm, Tolerances are in accordance to DIN EN ISO 9445.
Possible conditions for delivery are:
Solution annealed (soft) in accordance to DIN EN 10 088 – part 2, procedure 2R, or work hardened (hard) in
accordance to DIN EN 10151 procedure 2H with tensile strength up to maximum 1800 MPa.

 

Grade Solution Annealed

+C1000

1/2H

+C1150

3/4H

+C1300

4/4H

+C1500

5/4H

+C1700

K1

1.4568 Tensile strength 800~1000 Mpa 1000~1150 Mpa 1150~1300 Mpa 1300~1500 Mpa 1500~1700 Mpa 1700~1900 Mpa

 

For Details, please Contact

 

WUXI GUANGLU Special Steel Co., Ltd.

Stainless martensitic • precipitation hardening steel • stainless ferritic — Our answer to your needs

Tel: +86 510 81812873

Email: export@guanglusteel.com

 
EN 1.4568 DIN X7CrNiAl17-7 SUS631 Cold Rolled Stainless Steel Strip In Coil 0

Contact Details
Wuxi Guanglu Special Steel Co., Ltd

Contact Person: Paul Lu

Tel: +8615190257143

Send your inquiry directly to us (0 / 3000)